High Phos Electroless Nickel Plating Services Mid Phos Electroless Nickel Plating Services Low Phos Electroless Nickel Plating ServicesElectroless Nickel with Teflon Plating Services Electroless Nickel with Silicon Carbide Plating Services Bright Nickel Plating ServicesGold Plating Services Silver Plating Services Copper & Bright Acid Copper Plating Services Chemical Film Chromate Conversion Aloddine/Iridite Services Passivation Services Pre & Post-Treatment Secondary Services

Electroless Nickel with Silicon Carbide Plating Services

(click on thumbnail to enlarge)

Click to enlarge
Electroless Nickel with Silicon Carbide Plating Services

TWR Service Corporation also provides mid-phosphorus electroless nickel plating embedded with Silicon Carbide particles (ENSC). Composite carbide coating is a unique technology for carbide integration throughout a proprietary, autocatalytic, nickel alloy. Silicon carbide is one of the hardest materials on earth, with a published hardness four times that of hard chrome plating and nitrided steel. When dispersed in an EN matrix, the characteristics of high wear resistance and uniform deposition are achieved. The ingenuity of the matrix is in its of wear & abrasion, particle size, geometry and dispersion, to create the physical properties of carbide, on all conforming surfaces.

Rivaling hard chrome plating, TWR has achieved ENSC taber wear test results with an average TWI of 3.1. As with EN-PTFE, the silicon carbide particles are distributed throughout the entire nickel matrix, continually exposing carbide particles as the plating is worn.

Electroless Nickel Silicon Carbide Spec Sheet

Request Information

Electroless Nickel with Silicon Carbide Plating Services Capabilities

Specification
AMS 2404
ASTM B733
MIL-C-26074
Substrates
Aluminum
Brass
Copper Alloys
Leaded and Non-leaded Steel
Stainless Steel
Tool Steel
Plating Thickness 0.000050 " to 0.0035"
Quality Assurance Mil-C-45662
Mil-I-45208 with the inspection schedules in accordance with Mil Std.105
Mil-Q-9858
Order Quantity From single-quantity/prototype to production orders
Typical Lead Time 3 Working Days ARO Standard
Expedited Same Day Service (On Request)

Properties

Hardness After Heat Treatment - 850-950HK100
As Plated - 525-600HK100